Decomposition of ammonium sulfate residue in a high solid/gas ratio suspension state with an industrial-scale reactor system (production line)
2015
Abstract Ammonium sulfate residue is a particulate solid and is produced during the manufacture of ammonium sulfate fertilizer. The residue used in this study contained a large portion of calcium carbonate, from which active lime (CaO) was recovered via thermal decomposition. We used a purpose-built device to decompose the residue in a semi-suspension state. We found that CaO had the highest activity when residue was decomposed at 850–900 °C. Our experiments indicated that ammonium sulfate residue should be decomposed in a suspension state to produce active CaO. Based on our laboratory test findings, an industrial-scale production line with a high solid/gas ratio in a suspension state was d…
Alkaline treatment as a means to boost the activity of TiO(2)in selective photocatalytic processes
2020
In this work, the activity enhancement of TiO(2)photocatalysts by alkaline treatment has been investigated. Commercial (BDH, U.K., anatase phase) TiO(2)samples, treated in alkaline solutions of NaOH at different concentrations and temperatures, were tested for the photocatalytic partial oxidation of 3-pyridinemethanol in water under UVA irradiation to form vitamin B-3. Photocatalyst characterization has been carried out by XRD, BET, TEM, TGA, photoluminescence, FTIR, Raman, DRS, EPR and photocurrent measurements. The alkaline-treated samples showed an increased activity of up to 7 times (by considering first order rate constant values) compared to untreated BDH and the superior performance …
A comparative study of the photocatalytic activities of iron-titanium (IV) oxide photocatalysts prepared by various methods; spray pyrolysis, impregn…
1995
Abstract A series of iron/titanium oxide photocatalysts of varying Fe 3+ content have beenprepared by a number of different methods and subjected to controlled thermal treatment. Specimens have been characterised in terms of their crystalline structure and morphology, and indicate solid solutions containing both the anatase and rutile phases of TiO 2 , together with the formation of pseudo-brookite in some specimens. Intrinsic photo-activity measurements have been performed using a standard liquid-phase photocatalytic reaction. Results indicate that the photocatalytic activity of the specimens differs according to the method of preparation, and that all solids containing iron (III) species …
Polyacrylonitrile block copolymers for the preparation of a thin carbon coating around TiO2 nanorods for advanced lithium-ion batteries.
2013
Herein, a new method for the realization of a thin and homogenous carbonaceous particle coating, made by carbonizing RAFT polymerization derived block copolymers anchored on anatase TiO2 nanorods, is presented. These block copolymers consist of a short anchor block (based on dopamine) and a long, easily graphitizable block of polyacrylonitrile. The grafting of such block copolymers to TiO2 nanorods creates a polymer shell, which can be visualized by atomic force microscopy (AFM). Thermal treatment at 700 °C converts the polyacrylonitrile block to partially graphitic structures (as determined by Raman spectroscopy), establishing a thin carbon coating (as determined by transmission electron m…
Investigation on sol–gel synthesized Ag-doped TiO2 cermet thin films
2005
Abstract Undoped TiO 2 and Ag–TiO 2 (up to 23 at.% Ag) cermet thin films and polycrystalline powders have been prepared by sol–gel process. Their structure, composition, surface morphology and optical properties have been investigated by X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and ultraviolet–visible spectroscopy (UV–VIS spectroscopy). It has been observed that while Ag does not form a solid solution with TiO 2 , it promotes the anatase to rutile phase transformation. The transformation temperature decreases from 827 °C for undoped TiO 2 to about 650 °C fo…
Nanostructured Solids from Freeze-Dried Precursors: Multigram Scale Synthesis of TiO2 -Based Powders
2012
Nanocrystalline TiO2 and Ti1−xVxO2 (x = 0.01) powders have been prepared by thermal decomposition, in air, of amorphous precursors resulting from the freeze-drying of appropriate solutions. In addition, TiO2−xNy (anatase and rutile) and TiOxNy (rock-salt) have been prepared by thermal treatment in ammonia of a crystalline precursor (TiO2 obtained at 673 K). TEM and SEM images, as well as the analysis of the X-ray diffraction (XRD) patterns, show the nanoparticulated character of those solids obtained at low temperatures, with typical particle sizes in the 10–20 nm range when prepared at 673 K. The UV–Vis results indicate both the insertion of V in the anatase lattice and the feasibility of …
Sol-gel derived anatase TiO2: morphology and photoactivity
1994
Abstract High-surface area TiO 2 (anatase) was prepared by the sol-gel method and characterized by various instrumental and analytical methods, including X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, porosimetry, specific surface area measurements, scanning electron microscopy, and titration of surface hydroxyl groups. The specimen was tested for photodegradation of phenol and nitrophenols carried out in aqueous suspension at pH = 3; photoactivity was compared with that of commercially available anatase TiO 2 . Results are discussed in terms of porosity, surface area, and availability and population of surface OH groups, consequent upon the particular method used for…
Thermal resistance and upper lethal temperatures of underyearling Lake Inari Arctic charr
1997
Underyearling Arctic charr were acclimated to six temperatures between 6 and 21·5°C and thermal tolerance and resistance were tested after an acclimation period of at least 2 weeks. Resistance times were influenced by acclimation temperature and the highest upper incipient lethal temperature was 23–24°C. An upper limit for cultivation of Lake Inari charr is suggested to be 21°C which is the intercept of the function which represents the upper limit of the thermal tolerance zone.
Annealing of radiation induced oxygen deficient point defects in amorphous silicon dioxide: evidence for a distribution of the reaction activation en…
2011
The selective annealing of point defects with different activation energies is studied, by performing sequences of thermal treatments on gamma irradiated silica samples in the temperature range 300-450 °C. Our experiments show that the dependence on time of the concentration of two irradiation induced point defects in silica, named ODC(II) (standing for oxygen deficient centre II) and the E(γ)(') centre, at a given temperature depends on the thermal history of the sample for both of the centres studied; moreover in the long time limit this concentration reaches an asymptotic value that depends on the treatment temperature alone. These results suggest the existence of a distribution of the a…
Role of Water During Crystallization of Amorphous Cobalt Phosphate Nanoparticles
2016
The transformation of amorphous precursors into crystalline solids and the associated mechanisms are still poorly understood. We illuminate the formation and reactivity of an amorphous cobalt phosphate hydrate precursor and the role of water for its crystallization process. Amorphous cobalt phosphate hydrate nanoparticles (ACP) with diameters of ∼20 nm were prepared in the absence of additives from aqueous solutions at low concentrations and with short reaction times. To avoid the kinetically controlled transformation of metastable ACP into crystalline Co3(PO4)2 × 8 H2O (CPO) its separation must be fast. The crystallinity of ACP could be controlled through the temperature during precipitati…